Dial marker rings too thick.
$358
But date, ring markers and flat triangle are known issues of DSSD's REPs, Am I right?
Is it SS 316F and "swiss" mvmt?
$358
But date, ring markers and flat triangle are known issues of DSSD's REPs, Am I right?
Is it SS 316F and "swiss" mvmt?
Not sure about the 316F right now.
Yes, swiss mvmt.
CASE MATERIAL: Solid 316F Stainless Steel
Advice: next time don't buy 316F , just 316L
And don't buy "Swiss", just Asian clone no decorated
You will have the same or better quality and you will save a lot of money
Don't worry. Your purchase quality is OK but you have paid much money. OK?
For more information about that, read:
SS 316L vs. 316F vs. 904L- The final VERDICT- A technical study ("Outstanding post" Award )
http://forum.replica-watch.info/vb/showthread.php/ss-316l-vs-316f-vs-82263
Rules to choose a Milgauss rep
http://forum.replica-watch.info/vb/showthread.php/rules-choose-milgauss-rep-pics-81731.htm
Some rules for movements and steels of Milgauss are valid for DSSD.
Enjoy your DSSD it is a very good quality watch.
Not in all cases..
Look at pt's V7..
There is one for sale right now..You can get a new one though for 198$..
There is always the T4d which is a really nice also and pretty much the same..
The best you can do IMO though, is buy both a t4d and a noob,it does have a better case and bracelet, make one with the correct parts and sell the rest..
Am i correct??
Thats what i would do today..Then a pearl mode and superlume and ready.. lol
Enjoy your DSSD it is a very good quality watch.
Anyway, this DSSD is not for me, is for a relative. I have a V3 and I'm tihinking, it is time to improve it. What would you do in that case?
Thank you all for your comments
Not in all cases..
Look at pt's V7..
There is one for sale right now..You can get a new one though for 198$..
There is always the T4d which is a really nice also and pretty much the same..
The best you can do IMO though, is buy both a t4d and a noob,it does have a better case and bracelet, make one with the correct parts and sell the rest..
Am i correct??
Thats what i would do today..Then a pearl mode and superlume and ready.. lol